WD-SJ301埋弧焊用燒結焊劑WD-SJ301 SAW FLUX
所屬分類
碳鋼焊劑
產品描述
符合標準：
GB/T 5293-1999 F4A2-H08A F7A0-EM12K
AWS A5.17-2004 F6A0-EL8 F5A2-H08MnA
說明：WD-SJ301是硅鈣型中性燒結焊劑，堿度約1.0（BIIW），為球形顆粒，粒度為10-60目。特別適用于焊接各種類型的環縫，焊接時 形成短渣，即使焊接直徑較小的圓筒時也不淌渣?？山恢绷鲀捎?，直流 時焊絲接正極。焊接時可采用單絲、雙絲或多絲。
用途：可用于船舶、壓力容器、貯罐、鋼結構、螺旋焊管等結構的 焊接。推薦用于焊接20mm以下的低碳鋼及低合金鋼結構。
焊劑參考成分（%）：
熔敷金屬力學性能：
注意事項：
1、焊劑如果受潮，在使用前須經300~350℃烘焙2小時。 2、焊接處須清除鐵銹、油污、水分等雜質。
WD-SJ301 Agglomerated Flux For S.A. Welding
Standards: EN760 A CS 1 98 AC H5
GB/T 5293-1999 F4A2-H08A AWS A5.17-2004 F6A0-EL8
F5A2-H08MnA F7A0-EM12K
Introduction
WD-SJ301 is an agglomerated calcium-silicate type flux with a basicity index of BIIW 1.0. The flux is spherical granular, grain size is from 10 to 60 mesh. It has excellent welding technology properties. Regularly shaped welds are deposited without reduction of area or interface notches. Slag detachability is good. A short slag is produced, thus allowing circumferential welding on small-diameter cylinders without the risk of uncontrolled slag. WD-SJ301 can be welded with AC or DC at up to 1200A (single-wire process). The production of large pipes (especially spiral pipe welding) is a typical application for this flux. Relatively high manganese pick-up is obtained, thus allowing the flux be used with wires with a low Mn content. The special production method ensures that the flux has low moisture pick-up and granular stability. Flux shall be capable of meeting the applied requirements. As the bulk density is low, so is the consumption rate.
Applications
Flat butt and fillet welding for steel frames, bridges, spiral pipes, pressure vessels and ships.
Characteristics
It has excellent welding technology properties. Regularly shaped welds are deposited without reduction of area or interface notches. Welding defects such as pits and blowholes scarcely
occur when steel plate is thin. Bead is smooth with beautiful appearance. It is suitable for welding of less than 20mm steel plate.
Main Constituents (%)